S-4301.I

Thép nhẹ S-4301.I

Type Ilmenite
Industry Shipbuilding|Steel Fabrication
JIS Z3211 E4319
EN ISO 2560-A - E35 2 RA 1 2
KS D7004 E4301
AWS A5.1/ASME SFA-5.1 E6019
Catalog MSDS TTR
  • Caution .
  • Purpose ① General fabrication

    ② Shipbuilding

    ③ Suitable for High impact value required parts
  • Attribute ① Suitable for butt and fillet welding of thin and medium-thick plates (up to 20mm)

    ② Good crack resistance, pitting resistance

    ③ Good X-ray performance

S-7016.M

Thép nhẹ S-7016.M

Type Low-hydrogen Type
Industry Steel Fabrication
JIS Z3211 E4316
EN ISO 2560-A - E42 2 B 1 2
KS D7004 E4316
AWS A5.1/ASME SFA5.1 E7016
Catalog MSDS TTR
  • Caution ① Dry the electrodes at 300~350℃(572~662℉) for 60 minutes before use.

    ② Adopt back step method or strike the arc on a small steel plate prepared for this particular purpose to prevent blow hole at the arc starting."
  • Purpose ① Heavy steel fabrication
    ② Shipbuilding
    ③ Pressure vessels
  • Attribute ① Suitable for butt and fillet welding of heavy structure
    ② Good X-ray performance
    ③ Good mechanical properties

S-7016.O

Thép nhẹ S-7016.O

Type Low-hydrogen Type
Industry Pipe & Pipeline
JIS Z3211 E4316
EN ISO 2560-A - E42 2 B 1 2
KS D7004 E4316
AWS A5.1/ASME SFA5.1 E7016
Catalog MSDS TTR
  • Caution ① Dry the electrodes at 300~350℃(572~662℉) for 60 minutes before use.

    ② Stop the arc after moving the crater to the side wall of the groove.

    ③ Keep the arc as short as possible."
  • Purpose ① Pipe line
  • Attribute ① Suitable for one side welding of pipe

    ② Stable arc

    ③ Relatively low current

S-7024.F

Thép nhẹ S-7024.F

Type High recovery Rutile
Industry Steel Fabrication
JIS Z3211 E4324
EN ISO 2560-A - E42 0 RR 7 4
KS
AWS A5.1/ASME SFA5.1 E7024
Catalog MSDS TTR
  • Caution ① The optimum speed ratio is 1~1.5%.

    ② Usability degrades when moistened. In case of absorbing moisture, it must be dried. [70~100℃(158~212℉), 30~60minutes]
  • Purpose ① Heavy steel fabrication

    ② Shipbuilding
  • Attribute ① Highly efficient fillet welding

    ② High welding speed

    ③ Good bead appearance

    ④ Easy to remove slag

S-7014.F

Thép nhẹ S-7014.F

Type High recovery Rutile
Industry Steel Fabrication
JIS
EN ISO 2560-A - E42 0 R 1 2
KS
AWS A5.1/ASME SFA5.1 E7014
Catalog MSDS TTR
  • Caution ① Dry the electrodes at 70~100℃(158~212℉) for 30~60 minutes before use.

    ② Pay attention not to exceed the range of proper currents.
  • Purpose ① General fabrication
  • Attribute ① High welding speed

    ② Easy horizontal fillet and groove welding

S-6027.LF

Thép nhẹ S-6027.LF

Type High recovery Rutile
Industry Steel Fabrication
JIS Z3211 E4327
EN ISO 2560-A - E38 0 R 1 4
KS D7004 E4327
AWS A5.1/ASME SFA5.1 E6027
Catalog MSDS TTR
  • Caution ① In case of manual welding, operate by contact welding.

    ② In case of gravity welding, the optimum speed ratio is 1.2~1.5.

    ③ Dry the electrodes at 70~100℃(158~212℉) for 30~60 minutes before use
  • Purpose ① General fabrication
  • Attribute ① Suitable for butt and fillet welding of thin plates

    ② Good at vertical down

    ③ Good bead appearance

    ④ Good restriking

    ⑤ Easy to remove slag

S-6013.V

Thép nhẹ S-6013.V

Type Rutile-Cellulosic
Industry Steel Fabrication
JIS Z3211 E4313
EN ISO 2560-A - E38 0 RC 1 1
KS D7004 E4313
AWS A5.1/ASME SFA5.1 E6013
Catalog MSDS TTR
  • Caution ① In case of vertical downward welding, manipulate the electrode, keeping its tip in contact with base metal as shown in the sketch.

    ② Dry the electrodes at 70~100℃ (158~212℉) for 30~60 minutes before use.
  • Purpose ① General fabrication
  • Attribute ① Suitable for butt and fillet welding of thin plates

    ② Good at vertical down

    ③ Good bead appearance

    ④ Good restriking

    ⑤ Easy to remove slag

S-6013.LF

Thép nhẹ S-6013.LF

Type Rutile
Industry Steel Fabrication
JIS Z3211 E4313
EN ISO 2560-A - E38 0 R 1 2
KS D7004 E4313
AWS A5.1/ASME SFA5.1 E6013
Catalog MSDS TTR
  • Caution ① Dry the electrodes at 70~100℃(158~212℉) for 30~60 minutes before use.

    ② Pay attention not to exceed the range of proper currents.
  • Purpose ① General fabrication
  • Attribute ① Suitable for butt and fillet welding of thin plates ② Good restriking

    ② Good bead appearance

    ③ Easy to remove slag

    ④ Smooth arc and low fume

    ⑤ AC welding with low ocv

S-6011.D

Thép nhẹ S-6011.D

Type Cellulosic
Industry Steel Fabrication
JIS Z3211 E4311
EN ISO 2560-A - E38 0 C 1 1
KS D7004 E4311
AWS A5.1/ASME SFA5.1 E6011
Catalog MSDS TTR
  • Caution ① Pay attention not to use currents exceeding the recommended currents.

    ② As this electrode is prone to absorb moisture, store it with care.
  • Purpose ① Pipe line

    ② General fabrication

    ③ Shipbuilding
  • Attribute ① Standard in the pipe welding industry

    ② Deep penetration

    ③ High ductility (root pass)

    ④ AC and DC welding

S-6010.D

Thép nhẹ S-6010.D

Type Cellulosic
Industry Pipe & Pipeline
JIS Z3211 E4310
EN ISO 2560-A - E38 0 C 2 1
KS
AWS A5.1/ASME SFA5.1 E6010
Catalog MSDS TTR
  • Caution ① Pay attention not to use currents exceeding the recommended currents.

    ② As this electrode is prone to absorb moisture, store it with care.
  • Purpose ① Pipe line

    ② General fabrication
  • Attribute ① Standard in the pipe welding industry

    ② Deep penetration

    ③ High ductility (root pass)

S-4303.T

Thép nhẹ S-4303.T

Type Lime-Titania
Industry Steel Fabrication
JIS Z3211 E4303
EN ISO 2560-A - E38 0 RA 1 2
KS D7004 E4303
AWS
Catalog MSDS TTR
  • Caution ① Dry the electrodes at 70~100℃(158~212℉) for 30~60 minutes before use.

    ② Pay attention not to exceed the recommended range of currents.
  • Purpose ① Suitable for butt and fillet welding of thin plates

    ② Good restriking properties and high welding efficiency

    ③ Suitable for tack welding

    ④ Good mechanical properties
  • Attribute ① S-4303.T is a lime-titania type electrode used for welding in all positions. Iron powder contained in

    the coating ensures both good restriking properties and high welding efficiency.

    ② It is suitable for tack welding and intermittent welding.

    ③ Mechanical properties of all-weld metal are also good.

S-4303.V

Thép nhẹ S-4303.V

Type Lime-Titania
Industry Steel Fabrication
JIS Z3211 E4303
EN ISO 2560-A - E38 2 RA 1 2
KS D7004 E4303
AWS
Catalog MSDS TTR
  • Caution ① Dry the electrodes at 70~100℃ (158~212℉ ) for 30~60 minutes before use.

    ② As arc-restriking properties are not so good, it is suitable for intermittent welding.
  • Purpose ① General fabrication

    ② Shipbuilding

    ③ Automotive, Bridges & Construction
  • Attribute ① Suitable for butt and fillet welding of thin plates

    ② Good at vertical down

    ③ Good at vertical up

    ④ Good mechanical properties