S-86LTH

Стали работающие при низких температурах S-86LTH

Type Basic
Industry Offshore structure
JIS
EN
KS
AWS A5.5/ASME SFA5.5 E8016-G
Catalog MSDS TTR
  • Caution ① Dry the electrodes at 350~400 ℃(662~752℉) for 60 minutes before use.
    ② Preheat at 100~150℃(212~302℉). The temperature varies in accordance with plate thickness and kind of steel.
    ③ Adopt back step method or strike the arc on a small steel plate prepared for this particular purpose because arc striking on the base metal is in danger of initiating cracking.
    ④ Pay attention not to exceed proper heat-input because excessive heat-input causes deterioration of impact values of all weld metal.
  • Purpose ① OffShore Structure
    ② LPG vessel
    ③ LPG storage
    ④ Heat Exchanger
  • Attribute ① 55kg grade low-hydrogen high tensile electrode (-60°C)
    ② Ni, Ti, B contained in the weld-metal.
    ③ Great tensile strength in low-temperature
    ④ Anti- Low temperature crack (Low hydrogen)

S-8018.C3

Стали работающие при низких температурах S-8018.C3

Type Basic
Industry Offshore structure
JIS Z3211 E5518-N2
EN ISO 2560-A - E46 4 1Ni B 3 2
KS
AWS A5.5/ASME SFA5.5 E8018-C3
Catalog MSDS TTR
  • Caution ① Dry the electrodes at 350~400℃(662~752℉) for 60 minutes before use.


    ② Adopt back step method or strike the arc on a small steel plate prepared for this particular purpose, because arc striking on the base metal is in danger of initiating cracking.


    ③ Preheat at 80~100℃(176~212℉) before use. The temperature to be applied varies in accordance with plate thickness and steel kind.
  • Purpose ① Low temperature strength steel (1% Ni) • Offshore structure
  • Attribute ① Good impact value at -40°C


    ② Iron powder and low hydrogen type electrode (high efficiency

S-8018.C1

Стали работающие при низких температурах S-8018.C1

Type Basic
Industry Offshore structure
JIS Z3211 E5518-N5 AP L
EN ISO 2560-A - E46 5 1Ni B 3 2
KS
AWS A5.5/ASME SFA5.5 E8018-C1
Catalog MSDS TTR
  • Caution ① Dry the electrodes at 350~400 ℃(662~752℉) for 60 minutes before use.


    ② Preheat at 80~100℃(176~212℉).


    ③ Keep the arc as short as possible.
  • Purpose ① Low temperature strength steel (2.5% Ni)


    ② Offshore structure
  • Attribute ① Good impact value at -60°C


    ② Iron powder and low hydrogen type electrode (high efficiency

S-8016.C3

Стали работающие при низких температурах S-8016.C3

Type Basic
Industry Offshore structure
JIS Z3211 E5516-N2
EN ISO 2560-A - E46 4 1Ni B 1 2
KS
AWS A5.5/ASME SFA5.5 E8016-C3
Catalog MSDS TTR
  • Caution ① Dry the electrodes at 350~400℃(662~752℉) for 60 minutes before use.


    ② Adopt back step method or strike the arc on a small steel plate prepared for this particular purpose to prevent blowhole at the arc starting.


    ③ Pay attention not to exceed proper heat-input because excessive heat-input causes deterioration of impact values of all weld metal.
  • Purpose ① Low temperature strength steel (1% Ni)


    ② Offshore structure
  • Attribute ① Good impact value at -40°C

S-8016.C2

Стали работающие при низких температурах S-8016.C2

Type Basic
Industry Offshore structure
JIS Z3211 E5516-N7 AP L
EN ISO 2560-A - E46 6 3Ni B 1 2
KS
AWS A5.5/ASME SFA5.5 E8016-C2
Catalog MSDS TTR
  • Caution ① Dry the electrodes at 350~400 ℃(662~752℉) for 60 minutes before use.


    ② Preheat at 100~150℃(212~302℉). Preheat temperature varies in accordance with the plate thickness and steel kind.


    ③ Keep the arc as short as possible.
  • Purpose ① Low temperature strength steel (3.5% Ni)


    ② Offshore structure
  • Attribute ① Good impact value at -60~-75°C

S-8016.C1

Стали работающие при низких температурах S-8016.C1

Type Basic
Industry Offshore structure
JIS Z3211 E5516-N5 AP L
EN ISO 2560-A - E46 5 2Ni B 1 2
KS
AWS A5.5/ASME SFA5.5 E8016-C1
Catalog MSDS TTR
  • Caution ① Dry the electrodes at 350~400 ℃(662~752℉) for 60 minutes before use.


    ② Adopt back step method or strike the arc on a small steel plate prepared for this particular purpose because arc striking on the base metal is prone to initiating cracking.


    ③ Keep the arc as short as possible.


    ④ Preheat at 80~100℃(176~212℉). The temperature varies in accordance with the plate thickness and possible.


    ⑤ If each welded pass becomes thicker than acceptable level by high amperage or low speed ratio manipulation, the impact values and yield points will decrease."
  • Purpose ① Low temperature strength steel (2.5% Ni)


    ② Offshore structure
  • Attribute ① Good impact value at -60°C

S-7016.LS

Стали работающие при низких температурах S-7016.LS

Type Basic
Industry Shipbuilding|Offshore Structure
JIS Z3211 E4916-N1 AP L
EN ISO 2560-A - E46 6 1Ni B 1 2
KS D7023 DL5016-6AP1
AWS A5.5/ASME SFA5.5 E7016-G
Catalog MSDS TTR
  • Caution .
  • Purpose ① Low temperature strength steel


    ② Offshore structure


    ③ LPG, LNG storage tank
  • Attribute ① Extra low hydrogen electrode


    ② Good impact value at -60°C


    ③ CTOD properties at -10°C (14°F) temperature

S-76LTH

Стали работающие при низких температурах S-76LTH

Type Basic
Industry Shipbuilding|Offshore Structure
JIS Z3211 E4916-N1 AP L
EN ISO 2560-A - E42 6 Z1Ni B 1 2 H5
KS D7023 DL5016-6AP1
AWS A5.5/ASME SFA5.5 E7016-G
Catalog MSDS TTR
  • Caution .
  • Purpose ① Low temperature strength steel


    ② Offshore structure


    ③ LPG, LNG storage tank
  • Attribute ① Low temperature strength steel


    ② Offshore structure


    ③ LPG, LNG storage tank

S-7018.1H

Стали работающие при низких температурах S-7018.1H

Type Basic
Industry Shipbuilding|Offshore Structures|Steel Fabrication
JIS Z3211 E4918 H5
EN ISO 2560-A - E42 4 B 3 2 H5
KS D7006 E5016
AWS A5.1/ASME SFA5.1 E7018-1 H4R
Catalog MSDS TTR
  • Caution .
  • Purpose ① Heavy steel fabrication


    ② Low temperature strength steel


    ③ Offshore structure
  • Attribute ① Extra low hydrogen electrode


    ② Good impact value at -45°C


    ③ Vacuum sealed package available (HDM ≤ 4ml/100g)

S-7018.1

Стали работающие при низких температурах S-7018.1

Type Basic
Industry Shipbuilding|Offshore Structures|Steel Fabrication
JIS Z3211 E4918
EN ISO 2560-A - E42 4 B 3 2
KS D7006 E5016
AWS A5.1/ASME SFA5.1 E7018-1
Catalog MSDS TTR
  • Caution ① Dry the electrodes at 350~400℃(622~752℉) for 60 minutes before use.


    ② Keep the arc as short as possible, and avoid large width of weaving.


    ③ Adopt back step method or strike the arc on a small steel plate prepared for this particular purpose to prevent blow hole at the arc starting.
  • Purpose ① Heavy steel fabrication


    ② Low temperature strength steel


    ③ Offshore structure
  • Attribute ① Suitable for butt and fillet welding of thin and medium-thick plates (up to 20mm)


    ② Iron powder and low hydrogen type electrode (high efficiency)


    ③ Good impact value at -45°C